Synthesis, characterization and application of supported nickel catalysts for the hydrogenation of octanal.

Thumbnail Image



Journal Title

Journal ISSN

Volume Title



Three nickel based catalysts were prepared by the impregnation method (Ni/Al2O3 and Ni/SiO2) and co-precipitation method (Ni/ZnO). The catalysts were characterized by XRD, ICP-OES, BET-surface area and pore volume, SEM, TEM, TPR, NH3-TPD and in-situ XRD reduction. The catalytic activity of the catalysts in the liquid phase hydrogenation of octanal was studied at 110 °C and 50 bar. The effect of water as a co-feed on the catalytic activity of the catalysts was also investigated. Generally, all the catalysts were crystalline materials. The Ni/Al2O3 and Ni/ZnO catalysts contained NiO species that were “hard” to reduce, whereas the Ni/SiO2 catalyst was the easiest to reduce, according to the TPR and in-situ XRD reduction studies. The total acidity (μmol NH3/gcatal.) of the catalysts decreased in the following sequence: Ni/Al2O3 > Ni/ZnO > Ni/SiO2. The Ni/SiO2 and Ni/ZnO catalysts had intermediate and strong acidic sites, respectively, while the Ni/Al2O3 catalyst had weak-intermediate and strong acidic sites. The BET-surface area and pore volume of the catalysts decreased in the following order: Ni/Al2O3 > Ni/SiO2 > Ni/ZnO. The conversion of octanal for all the catalysts was ca. 90 %. The Ni/SiO2 and Ni/ZnO catalysts had octanol selectivities of over 99 % and the Ni/Al2O3 catalyst had 95 % octanol selectivity. The alumina support was observed to catalyze the formation of heavy products (C24 acetal, dioctyl ether and 2-hexyl-1-decanol). The water present in the feed poisoned the alumina sites that were responsible for the formation of heavy products thereby, making the catalyst more selective (> 99 %) to octanol. For the Ni/SiO2 catalyst the presence of water in the feed caused the octanal conversion to decrease with time-on-stream. The deactivation of the Ni/SiO2 catalyst, when water was used as a co-feed, was caused by the mechanical failure of the catalyst and also by the leaching of nickel metal during the reaction.


Thesis (M.Sc.)--University of KwaZulu-Natal, Durban, 2010.


Nickel catalysts., Octyl alcohol.